Alumina Castables Dealers in Ramdev Nagar, Ahmedabad

• Feature: Superior Resistance to Temperature

This castables posses our brand name DI ALCAST - A and are manufactured using a high purity high alumina cement produced and marketed by us.The number in the brand name denotes the percentage of alumina content in these castables.

We provide premium Alumina Refractory Castable used for hot face and back up linings. Our High Alumina Refractory Castables are highly appreciated for low thermal conductivity and low density that assist in conserving heat energy. We are dependable Supplier and Exporter of the Alumina Refractory Castable in Ahmedabad (Gujarat). Types Of Alumina Refractory Castable CT Heat Castables are produced in three grades designated as CT Heat-A, CT Heat-K and CT Heat-C containing the special high purity, high alumina refractory binder. Typical properties of these castables, including data on strength, conductivity and chemical composition are provided in the table at the bottom of this page. Each grade of CT Heat castables is used for a specific service temperature and environment. CT Heat-A : CT Heat-A is a high purity, high alumina castable of exceptional quality with alumina content of over 90% and with very low silica and iron contents. Hence, it is used for service temperatures up to 1750oC and can resist attacks from process gas atmospheres containing carbon monoxide and hydrogen.CT Heat-A is particularly suitable for use in coke ovens gas production plants as well as gasification plants and is also usedIn the Iron and Steel industry: For lining blast furnaces and for skew backs, ports and roof lining of arc-melting furnaces.In the non-ferrous metal industry: To line reverberatory furnaces where high purity aluminum is produced.In reactors of refineries as well as in fertilizer plants where castables with a high degree of resistance to carbon monoxide, hydrogen and ammonia are desired.For lining of pre-heaters/converters and on all transfer lines.CT Heat-K : CT Heat-K which has an alumina content of 60% can be used for service temperatures up to 1600oC. This castable also has a low iron content and can resist carbon monoxide attack. CT Heat-K can be used in: Blast furnacesFoundriesBoiler industry stoker archesLocations where reducing atmospheres are encountered.Construction of soak pit covers, forge furnaces, tunnel kilns, heat treatment furnace car tops as well as electro-phosphorus furnaces.CT Heat-C : CT Heat-C is a castable with about 50% alumina and serves as a general purpose high temperature castable required for service temperatures up to 1500oC. CT Heat-C is suitable for use in: Iron and steel industrySemi-permanent foundriesAnnealing furnacesStress relieving furnacesConstruction of special refractory shapes, monolithic convection sections in water tube boilers, ash-hopper linings and incinerator arches Packaging and Storage : CT Heat Castable is available in HDPE bags of 50kg. The shelf life of CT Heat castables is six to nine months under ideal storage conditions. Specifications Medium Purity Dense Castables CT Crete SuperProductCT Crete (Super)*Type70% Alumina CastableNature of BondHydraulicInstallationVibration castingGeneral Properties Raw Material BaseCalcined BauxiteMax. Service Temperature1450oMax. Grain Size1.5 mmWater required for casting10 ~ 11 %Reversible Thermal Expansion0.65% at 1000o Chemical AnalysisTypical ValueSpecificationAl2O3 %70.570.00 min.SiO2 %11.5-Fe23 %4.2 5.00 max.TiO2 %7.2-CaO6.1-LOI %0.3- Physical PropertiesTypical ValueSpecificationWater for trowel ling consistency %24 ~ 28-Water required for ramming consistency %10 ~ 20-Transverse strength after drying at 110 oC for 24 hours (kg/cm2)17-Retained above maximum size2 5.00 max. Thermal PropertiesTypical ValueSpecificationPyrometric cone equivalent (Orton/oC)32/171731.5/1699 Other DetailsPackaging50 Kg. bags-Storage life12 months-Delivery stateDry-

(1)DI ALCAST - A Super purity high alumina dense castables are being produced at our plant. This castables posses our brand name DI ALCAST - A and are manufactured using a high purity high alumina cement produced and marketed by us. The number in the brand name denotes the percentage of alumina content in these castables. Salient Features Highest Purity Excellent Strength Superior Resistance to Temperature Resist Fluctuations of Temperature Suitable for use in reducing atmospheres Service Temp. [ max ] - 1700 0C Chemical Properties A12O3 : 90% min. (2)DI AL - 90 K Chemical Analysis A12O3, % (min) : Fe2O3, % ( max) : 87.00 1.00 Size 0 - 0.2 mm Application Jointing Mortar for slide gate plate and nozzle. (3)DI ALCAST - K Super purity high alumina dense castables are being produced at our plant. This castables posses our brand name DI ALCAST - K and are manufactured using high purity high alumina cement produced and marketed by us. The number in the brand name denotes the percentage of alumina content in these castables. Salient Features Highest Purity Excellent Strength Superior Resistance to Temperature Resist Fluctuations of Temperature Suitable for use in reducing atmospheres Service Temp. [ max ] - 1600 0C Chemical Analysis AL2O3, %, [min] : Fe2O3, %, [max] : 60.00 1.20 (4)DI AL -95 H Chemical Properties A12O3 : 94% min. Size 0 - 5 mm Application Ramming Mass for fixing Ladle well Block